Readily dispersible dry gluten product and uses thereof

ABSTRACT

Powdered vital wheat gluten is difficult to disperse in water and a dispersion, once obtained, is unstable since individual particles readily coalesce with the formation of an intractable, lumpy mass. By converting the powdered gluten into novel structures in the form of agglomerates thereof under conditions which do not denature the gluten, the gluten can be readily wetted out and dispersed in water to form a relatively stable dispersion. Accordingly, the agglomerated gluten is ideally suited for the manufacture of yeast leavened bakery products, especially by continuous dough-making processes.

United States Patent Hampton et al.

READILY DISPERSIBLE DRY GLUTEN PRODUCT AND USES THEREOF Inventors: Richard John Hampton,

Pierrefonds; Jacques Robert Rolland, Bouchardville; Thomas Gallo, Toronto, all of Canada Assignee: Ogilvie Flour Mills Company Limited, Montreal, Canada Notice: The portion of the term of this patent subsequent to Nov. 28, 1989, has been disclaimed.

Filed: Jan. 7, 1974 Appl. No; 431,318

Related U.S. Application Data Continuation-impart of Ser. No. 309,656, Nov. 27, 1972, abandoned, which is a continuation of Ser. No. 26,405, April 7, 1970, Pat. No. 3,704,131.

U.S. Cl. 260/112 G; 426/653; 426/656 lnt. Cl. A23J 3/00 Field of Search 426/19, 23, 62, 147, 148,

* Dec. 9, 1975 [56] References Cited UNITED STATES PATENTS 3.362.829 1/1968 Landfried et al. 426/212 X 3,391,003 7/1968 Armstrong et al 426/453 X 3,704,13l 11/1972 Hampton et al. 426/453 Primary Examiner.lames R. Hoffman Attorney, Agent, or Firm-Christen & Sabol [57] ABSTRACT Powdered vital wheat gluten is difficult to disperse in water and a dispersion, once obtained, is unstable since individual particles readily coalesce with the formation of an intractable, lumpy mass. By converting the powdered gluten into novel structures in the form of agglomerates thereof under conditions which do not denature the gluten, the gluten can be readily wetted out and dispersed in water to form a relatively sta ble dispersion. Accordingly, the agglomerated gluten is ideally suited for the manufacture of yeast leavened bakery products, especially by continuous doughmaking processes.

4 Claims, 9 Drawing Figures Patent Dec. 9, 1975 Sheet 1 of 7 US. Patent Dec. 9, 1975 Sheet 3 of? 3,925,343

U.S. Patent Dec. 9, 1975 Sheet 4 of? 3,925,343

AJNEUSISNBI] E c: D (D U.S. Patent Dec. 9, 1975 Sheet 5 of7 3,925,343

U.S. Patent Dec. 9, 1975 Sheet 6 of? 3,925,343

AIJNEIISISNUI] 3 III 4 1 Q pi 7 W 7 n .1? V V i 3 V i V, r .n

US. Patent Dec. 9, 1975 Sheet 7 of7 3,925,343

AIJNHgISNUJ N55253:: ii

READILY DISPERSIBLE HRY GLUTEN PRODUCT AND USES THEREOF BACKGROUND OF INVENTION This invention relatesbroadly to a novel gluten prod uct and uses thereof. More particularly, this invention is concerned with a vital wheat gluten product of noveii physical structure endowing it with improved functionality, and to its utilisation in making different products, especially, though not exclusively, yeast-leavened bakery products.

Vital wheat gluten (sometimes referred to herein, for convenience, simply as gluten), is a concentrated natural protein in the form of a light tan powder having a bland taste and aroma. It usually contains 75 to 80% protein, 6 to 8% fat-like phospholipids and related compounds, some fiber, residuai starch, a small amount of mineral matter and between 4 and 6% residual moisture. It is normally insoluble in neutral aqueous solution (pH 4 to 8). For commercial purposes, vitai wheat gluten is presently manufactured by one of several washing processes in which wheat flour is kneaded with water to remove the starch and water-soluble materials from the gluten. During this treatment this gluten forms a tough, rubbery elastic mass containing a high proportion of water. This water must be removed rapidly without exposing the gluten to excessively high temperatures, since gluten, being a protein, can be denatured by exposure to high temperatures when in the wet state.

Two drying processes are in common use, one involv-- ing spray drying and the other flash drying. The gluten from the former method tends to be finer than the flash dried gluten which, typically, has an average particle size of between and 75 microns.

Vital wheat gluten is an increasingly important product of commerce, especially widelyvu ed today in the manufacture of yeast-leavened bakery products such as bread, rolls and buns. In this application, it supplements the natural flour protein where added strength is needed or desired for one or more of several reasons, say, to build stronger sidewalls in expanded white bread, or in the production of variety breads where the non-flour proteins dilute the flour protein to such an extent that the latter protein cannot function satisfactorily without supplementation. It is also used in other food applications-For instance, is is used to increase the protein content, and hence the strength, of pastalike products such as macaroni, and in the manufacture of dietary wafers. It is also used as a binder or diluent n pharmaceutical tablet formulations.

It is well known in the art that utilisation of vital wheat gluten in applications such as the manufacture of yeast-leavened bakery products, is hindered on account of the fact that it is not free-flowing or readily dispersible when added to water, and the dispersion, once obtained, is not very stable, having a marked tendency to lump and to coalesce. It is generally believed that this characteristic poor dispersibility can be attributed to two distinct, but inter-related, phenomena. Firstly, powdered gluten is highly hydrophilic so that upon initial wetting it hydrates rapidly to form discrete lumps consisting of a dough-like outer wall, which resists further moisture penetration, encapsulating a core of essentially dry unwetted and unaltered powdered gluten at the center. These lumps can be smoothed out and broken up, though vigorous agitation is needed for this purpose. However, the disintegration of the lumps and dispersal of the particles is accompanied by the wetting of individual gluten particles. These individual, wetted particles, because of significant inter-molecular forces, exhibit cohesion so that they tend to coalesce, when they can be separated only by the exertion of considerable disruptive forces. Accordingiy, a dispersion of ordinary powdered gluten once obtained is markedly unstable because of this tendency for coalescence between individual particles. Whatever the theoretical explanation, it is a fact, that on mixing vital wheat gluten with waiter, a lumpy product is obtained which, on vigorous agitation, is transformed into a highly intractable, rubbery, elastic mass.

Efforts have been made in the past to overcome, or to improve upon, the poor dispersibility of powdered vital wheat gluten. In essence, prior practice has involved intimately incorporating, or coating the powdered gluten with a small amount of certain selected materials, notably lipids. Lipids that have been used for this purpose include non-ionic hydrophilic lipids like monoglycerides, edible salts of lactylic esters of fatty acids, polyoxyethylene stearate, stearyl monoglyceride citrate, which provide a protective barrier or surface layer serving to reduce coalescencebetween particles of the thus-treated gluten. At the present time, a gluten coatedwith such a hydrophilic lipid, believed to be the nomoglyceride, glyceryl monostearate, is commercially available. This material is effective to the extent that the hydrophilic lipids alleviate to a marked degree the cohesion problem so that the treated gluten tends to form a relatively stable vdispersion once dispersed. However, it is found that the thus-treated gluten is of poor wettability so that on being added to water it does not disperse readily but instead tends to form a lumpy mass, requiring relatively vigorous agitation in order to disperse the individual gluten particles.

Also, the treated gluten, because of the presence of an additional, relatively expensive, material often in substantial amounts (typically around 20%), which needs to be applied in a carefully controlled process, is

significantly more expensive on a gluten basis than the untreated powdered gluten. This is a considerable deterrent to its widespread adoption by, for instance, the commercial baker who operates in a markedly cost conscious and highly competitive industry. This is further aggravated by the fact that the presence of a substantialarnount of anextraneous material reduces the effective amount of gluten, the component of primary interest to the baker, in a given weight of the product; this markedly reduces the water absorption of the gluten product, and can complicate the bakers standard formulations and procedures. Furthermore, the materials used in the treatment may detract in one way or another from desired properties in the food or other product in which the treated gluten product is incorporated.

SUMMARY OF THE INVENTION Broadly stated, we have now found, and this finding forms the basis for the present invention, that by converting ordinary powdered vital wheat gluten into a novel physical form, the resulting gluten product is readily wettable and provides a relatively stable neutral aqueous dispersion with a reduced tendency toward particle cohesion.

A primary object of this invention, therefore, is to provide a dry gluten product of improved wettability which, in its own right, i.e., without the incorporation of, or coating by, a specific material, for instance, a lipid, can be readily dispersed in neutral aqueous dispersion (about pH 4 to 8) to give a stable dispersion exhibiting little or no tendency to coalesce into a rubbery elastic mass.

Another object is to provide improvements in methods of making yeast-leavened bakery products using the dry gluten product of this invention.

FIGS. l and 2 are photomicrographs serving to illustrate the characteristic agglomerate structure of the improved gluten product in contrast with the individual particle character of ordinary commercially available vital wheat gluten;

FIG. 3 is a graph illustrating the results of mesh analyses of the agglomerated gluten, ordinary powdered gluten and a treated powdered gluten product of the prior art;

FIGS. 4 and 5 are photographs serving to illustrate the improved dispersibility of the agglomerated gluten in contrast with ordinary powdered gluten and a treated powdered gluten product of the prior art; and

FIGS. 6 to 9 are graphs showing Brabender farinograph curves of the agglomerated gluten product and, for comparative purposes, various other materials.

In fulfilment of the foregoing and related aims, this invention provides a dry, undenatured gluten product in the form of coarse, porous, irregularly-shaped agglomerates composed of a multiplicity of individual vital wheat gluten particles adhered together in a random form and array. The major proportion of these agglomerates, often more than 90% of the total, have a particle size exceeding 149 microns (retained on a I00 mesh screen) and are characterised by a unique combination of physical properties such that the gluten product is free-flowing and readily wettable, and can be rapidly dispersed in neutral aqueous medium (about pH 4 to about pH 8) by no more than relatively gentle stirring to form a relatively uniform and stable dispersion therein.

In the derivation of the agglomerated gluten product, ordinary powdered gluten is subjected to a treatment in which the individual gluten particles are exposed to the action of a wetting agent under controlled conditions which lead to the formation of the said coarse, porous, irregularly-shaped agglomerates. Formation of the porous agglomerates results in a decrease in bulk density. The moist material is then dried, under controlled conditions, to remove excess free moisture to give an agglomerated gluten of a defined residual moisture content, which preferably is no more than about 10%. Advantageously, the drying of the product is controlled to give a total moisture content in the product of between 6 and 10%, preferably between 6 and 8%, for it has been found that this moisture content is associated with optimum dispersibility, the agglomerated gluten dispersing quite spontaneously on addition to water.

This product, as will be discussed in more detail hereinafter, possesses a number of characteristic properties which distinguish it from ordinary powdered gluten, and which in particular makes it possible to readily and quickly disperse the material in water to form a relatively stable dispersion, with no more than gentle agitation.

DETAILED DESCRIPTION OF INVENTION This gluten starting material can be of any particular or conventional type, whether spray or flash-dried, and is characterised by its fine powder form and its nonfree-flowing properties reflected in a poor dispersibility, and a pronounced tendency for particle coalescence. The individual gluten particles range in size from about 5 microns to about [25 microns, (average particle size about 50 microns), depending, to some degree, on the method of' preparation.

This gluten is then subjected to a treatment wherein the individual particles are exposed to the action of a wetting agent so as to render the surfaces thereof sticky. The superficially agglutinated particles are then brought into intimate contact in such a way as to cause them to adhere together in the form of aggregates of random size and irregular shape, but always of a size substantially greater than the size of the individual particles constituting the initial gluten. The agglomerates are then dried to adjust the final residual moisture content to the preferred level of less than about l0%. Thereafter, the material is classified, and agglomerated gluten of the desired size and structure is delivered as a finished product and suitably packaged. Nonagglomerated and oversized material is recycled. The agglomerated gluten structures so-obtained are sufficiently strong and firm to withstand normal handling without giving rise to any serious disintegration problem.

In the wetting and drying steps, the conditions of time and temperature are selected and controlled to avoid any deleterious effect, as would, for instance, obtain were the gluten denatured, on the functional properties of the gluten in supplementing protein in food applications. Such conditions can be readily determined by means of a few trials.

Usually, the wetting agent is either a liquid which, on contact with the gluten, renders the gluten particles tacky and causes them to adhere together in clusters following contact, by hydrating part or all of the gluten or otherwise transforming it to obtain this effect, or a solution or suspension of some ingredient in a liquid, such, for example, as sugar solution, so that this ingredient itself performs the agglomerating function.

Conveniently, the wetting agent is water or water vapor, though other substances such, for example, as ethanol, formic acid, acetic acid and ammonia may be used.

In a preferred embodiment of this invention, the gluten particles are superficially agglutinated with the wetting agent, agglomerated and dried almost instantaneously in a single treatment zone, thus eliminating any need to transfer the wet sticky agglomerates from an agglomerating zone to a drying zone. This may be achieved by:

i. Forming the powdered gluten into a fluidized bed;

ii. Maintaining the bed in a particulate fluidized state by passing a fluidizing gas, such as compressed air, upwardly through the bed;

iii. Discharging a wetting agent in atomized form directly into the particulate, fluidized bed between the top and the bottom thereof. This wetting agent agglutinates the surfaces of the particles which are commingled, by the gentle agitation of particles in the bed, to an extent sufficient to cause such particles 'on contact with adjacent particles to adhere together in the form of moist, irregularly-shaped agglomerates; and

iv. Drying the agglomerates by means of the fluidizing gas, typically, by evaporation of the liquid therefrom to a residual moisture content of less than about The wetting, agglomerating and drying'follow in sequence but take place substantially instantaneously, and the agglomerates are then removed from the chamher.

This preferred process is further described and claimed in our copending application Ser. No. 26,405, filed on Apr. 7, 1970 which has now issued as U.S. Pat. No. 3,704,13l.

That gluten could be agglomerated using the technique described above is surprising. It is well known, as stated earlier, that dry gluten is extremely hydrophilic and generally when hydrated, becomes a sticky, elastic, tenacious, rubbery mess. It was to be expected therefore that a wetting process, such as agglomeration, would result in the formation of larger aggregates than desired and that such a formation process could not be easily controlled. The larger aggregates, once formed, would be too tough and tenacious to break apart into smaller particles by the fluidizing action alone. Also it was expected that such large aggregates would be difficult to maintain in a fluidized state with the remaining particulate dry gluten because of their weight and therefore these large aggregates would tend to collect at the bottom of the treatment chamber. This result would inter alia interfere with the entry of the fluidizing gas through the bottom of the treatment chamber in the preferred agglomerating process. it would also be expected that, due to the tenacious nature of the wetted gluten, nozzles through which the said wetting agent is introduced in an atomized state directly into the fluidized bed of gluten, would become fouled and plugged during the continued operation of the agglomerator.-

Such clogging would require complete shut-down to remove the nozzle obstruction. Such an occurrence, on a routine basis, is inconvenient and inefficient.

A further anticipated problem was the great difficulty in the partial or total removal of this added moisture, necessary for both hardening of the agglomerates and reduction of the product moisture content to a desired range upon the wetting and agglomeration of the powdered gluten. The moisture removal would easily be effected by the application of hot fluidizing gas in the agglomeration technique described above. However, in order to maintain the vitality of the gluten, that is, to prevent the denaturization and hence loss of functionality of the gluten, the temperature must be adjusted to prevent the temperature of the fluidized gluten from rising above about 60C., the temperature at which gluten begins to denature. It was to be expected therefore that the removal of moisture from the soft gluten agglomerates would prove to be very difficult in view of the requirement that' the bed temperature be maintained below the relatively low temperature of about 60C.

However, it was found surprisingly that workable operating conditions could be found which turned out, in retrospect, to be generally similar to the conditions employed to agglomerate other finely particulate substances, such as flour. it is apparent that the anticipated problems in the production of gluten agglomerates could be overcome and solved by the judicious selection and control of flow rates and temperatures which is deemed within the skill of the art. However, such process requirements, are apparent only after the surprising discovery that gluten could be agglomerated in the face of heretofore expected insurmountable problems related to the known hydrophilic behaviour of dry, powdered gluten.

As alternatives to the above-described preferred embodiment, the following treatment methods can also be employed to agglomerate gluten. The first method utilizes a conical cyclone feeder, through which the powdered gluten is conveyed by means of a carrier gas which deposits the gluten on the sides thereof. The gluten powder descends along the inclined sides of the cyclone through an outlet slot in a sheet-like form into an agglomerating chamber. The falling sheet-like gluten powder enters a wetting zone formed at the apex of a plurality of intersecting moisture sheets mounted at the top of the agglomerator. The moisture sheetsare directed downward into the agglomerating chamber. Air is admitted into the lower portion of the agglomerating chamber through slots to serve as a counterflow against the falling wetted gluten particles propelled by the injected moisture sheets. The resultant whirling action permits the wetted particles to undergo random collisions with other particles to form moist aggregates. These aggregates eventually pass through a smaller conical discharge port in the bottom of the agglomerating chamber into a heated chamber below to undergo partial drying. Further drying to any desired moisture content can be effected by passage via a conveyor arrangement into a conventional afterdryer. A more detailed description of a similar agglomeration method can be found in U.S. Pat. No. 3,313,629 of E. G. Thompson et al.

Another agglomeration method is described in U.S. Pat. No. 3,549,336 of T. Hodel. When using this method a falling stream of powdered gluten is contacted with a continuous horizontal thin film of jetted heated wetting agent, e.g., water. The wetted particles, by the action of the applied heated liquid jet, are caused to collide randomly with each other to form aggregates which are then carried along the path of the jet. Thereafter the aggregates fall by gravity through an outlet in the lower end of the agglomeration zone into a drier comprising a vibrating screen through which heated air.is passed.

A further agglomeration method which may be used to produce the agglomerated gluten product of the present invention is that described in Canadian Pat. No. 874,934 of .l. T. Hutton et al. The method essentially involves using a cyclone feeder wherein powdered glutten is air-blown to create a swirling effect. This particle movement pattern serves to separate lines from the bulk material as well as to distribute uniformly particles into the top of an externally heated agglomerating or treatment chamber. The feed material collects on the sides of the cyclone and moves down into the upper part of the treatment chamber as a powder cloud. The powder cloud falls into a moistening zone in which a nozzle or nozzles point downward through the centre of the inlet port and emits a high velocity stream of atomized wetting agent, e.g., water. A rolling, boiling movement of the powder throughout the chamber is created by the high velocity liquid stream. The moistened powder is carried downward into the lower portion of the chamber and then is carried upward again,

due to the convention type currents created. The moistened gluten powder in the system undergoes random collisions to form aggregates. The heavier aggregates eventually fall by gravity through a lower opening into a drier portion to effect the desired moisture level in the product.

Quite unexpectedly, it has been found, that the protein" quality of the agglomerated gluten of this invention obtained for example, by the above methods as compared with the quality of the conventional powdered gluten starting material is unimpaired and substantially unchanged so that, in this important respect, it performs in a normal manner when used in the manufacture, for instance, of yeastleavened bakery products. This is confirmed by the comparative tests detailed in Examples hereinafter. At the same time, the functionality, and hence the utility of the agglomerated gluten in such applications is enhanced because of the improved dispersibility and resistance to particle coalescence following dispersion, i.e., dispersion stability.

The agglomerated gluten of this invention, as discussed in detail below, has a characteristic structure, and a combination of desirable physical properties, which serve to distinguish it from gluten presently available. and a combination of desirable physical properties, which serve to distinguish it from gluten presently available. Structure Individual gluten agglomerates are composed of a multiplicity, typically between about 3 and about 25, of gluten particles bonded together in a random array to give a coarse, irregularly-shaped structure of marked porosity and with a surface area that is relatively large in relation to its bulk. The characteristic structure of the agglomerated gluten, and the contrast with powdered gluten are shown in the photomicrographs of FIGS. 1 and 2 in the accompanying drawings. FIG. 1 is a photomicrograph of a typical sample of the agglomerated gluten photographed at a magnification of 40x. It shows clearly the random aggregation of individual gluten particles into coherent irregularly-shaped structures. FIG. 2 is a photomicrograph, for comparative purposes, of commercially available powdered gluten, at the same magnification. This clearly shows that in contrast to the agglomerated gluten, the particles of gluten powder are inherently separate and detached and individually of a relatively regular shape with a low surface area relative to the bulk thereof.

PROPERTlES A. Size The size of the agglomerated gluten of this invention as recovered from the processes as described hereinbefore varies, though usually a major proportion, preferably more than 90%, of the agglomerates remain on a l mesh screen (all mesh sizes quoted herein refer to US. Standard Sieve sizes) and are of a size in excess of M9 microns. In contrast, 90% of the particles in powdered gluten pass through the same screen size.

The size of the agglomerates is thought to be an important factor in securing the desired characteristics of the product. Thus, when the agglomerates are ground so that they pass through a I00 mesh screen, the product does not have the desired characteristics in respect of, for instance, the ability to quickly and readily disperse in water without vigorous agitation to form a relatively stable dispersion. Thus, it is considered important for the bulk of the agglomerated gluten to be of a size such that it will remain on a sieve of a I00 mesh or less, or in other words is greater in size than 149 microns, and this is normally obtained with the preferred method described above under varying operating conditions. Individual particles of such size are easily discernible to the naked eye, whereas particles of powdered gluten are not.

An upper limit for particle size for practical purposes is set at about 500 microns. A preferred range of particle size is about 160 microns to about 250 microns. Clearly, the lower size limit is of greater importance in the determination of the desired product characteristics.

FIG. 3 illustrates the results of mesh analyses upon a typical sample of agglomerated gluten made in accordance with the present invention and, for comparative purposes, a typical sample of powdered gluten, and a typical sample of a commercially available product comprising powdered gluten coated with 20% by weight monoglyceride (treated gluten). The desired series of sieves were stacked in their respective order in the series, with the finest mesh size at the bottom. A gm. sample of the material to be tested was placed on the upper sieve, and the sieves placed in a Ro-Tap Sieve Shaker for 5 minutes. The material on each sieve was then weighed and the weight reported as a percentage of the total weight of material accounted for on the sieves and in the pan under the finest mesh size. Referring to FIG. 3, curve A represents the sieve analysis of the agglomerated gluten, curve B represents the sieve analysis of the powdered gluten, while curve C represents the screen analysis of the treated gluten. Essentially, these curves show the particle size distribution in the agglomerated gluten with the major proportion of a size in excess of 149 microns, in comparison with that of powdered gluten and treated gluten in which the bulk of the individual particles are of a size less than 149 microns.

B. Bulk Density The irregular shape and bulky nature of the agglomerated gluten is reflected in the bulk density thereof which is lower than the bulk density of powdered gluten, as determined by the following procedure:

The apparatus used was a Scott Volumeter (available from the Fisher Scientific Company). It comprised a large brass funnel with a metal screen, and a smaller funnel with a straight stem to direct the sifted gluten into a baffle box. This box had a series of glass baffle plates which regulated the fall of the gluten. A funnel at the bottom collected the gluten and directed it into a cubic inch receiver. This was a brass box with a capacity of exactly one cubic inch, and was supplied with a counterpoised weight. The gluten, sifted at the top, was baffled in its fall so that it actually entered the cubic inch receiver at the bottom under a constant head, which ensured the receiver being packed in the same manner each time. The receiver and contents were weighed and the weight of the gluten in the receiver obtained. The results (bulk density) were expressed in grams per cubic centimeter (gm./cc.).

A typical sample of agglomerated gluten with 92% of a particle size in excess of 149 microns, had a bulk density of.36 gm./cc/. which contrasted with a bulk density of .42 gm./cc. for powdered gluten.

Generally, the bulk density for agglomerated gluten according to the present invention and prepared, for example, by the foregoing preparative method ranges between about 0.33 and about 0.41 gm/cc, with a preferred range between about 0.34 and about 0.38 gm/cc.

C. Flo'wability Diameter I50 m'.m. Overall height I I60 m.m. Stern height l mm.

Stem diameter 40 'mm.

A stopper was fitted into the lowenend of the funnel stem to prevent premature release of the material. The stopper was then removed, and the time required for the entire sample to discharge from the funnel reported as the flowability rate in seconds. The results are tabulated below:

Table l Product Flowability (secs) Agglomerated gluten Average particle size 250 l2 Powdered gluten Would not flow Treated gluten 26 It is apparent from the above data that the agglomerated gluten has a markedly superior flowability compared to both prior art gluten products. The free-flowing character of the agglomerated gluten is reflected in the ease with which it can be removed from the package and poured without plugging or dusting.

D. wettability Dispersibiiity The enhanced wettability and dispersibility of the agglomerated gluten in contrast with powdered gluten as well as powdered gluten treated with by weight of a monoglyceride can be demonstrated as follows:

A 400 ml. low form Griffin beaker was filled to approximately one inch from the top with water at 20C. and a teaspoonful of each of the three materialsin turn carefully placed on the surface of the water. The dispersal time was reported as the number of seconds required for all of the material .to sink belowthe surface of the water: i

i. Agglomerated Gluten i When the teaspoonful of a typical sample of agglomerated gluten was placed onthe surface of the water, it floated thereon only transiently and progressive sinking occurred withina second or so. The dispersal time was 2 seconds. As the material sank toward the bottom of the beaker it disintegrated and dispersed without the need for even gentle stirring. In a short space of time (7 seconds), the bulk of the gluten was resting on the bottom of the beaker; gentle stirring recreated a uniform dispersion free from lumps.

ii. Powdered Gluten When the test was applied to this material, the bulk of it floated upon the surface of the water, and when the contents of the beaker were permitted to stand without stirring, the powder formed a lumpy, doughball-like, mass. The dispersal time could not be ascertained since the bulk of the material never sank below the surface. On hand stirring the contents of the beaker, an intractable, elastic mass of hydrated gluten was formed instead of the powder dispersing to form a uniform slurry. In fact, even vigorous agitation was not effective in breaking up the lumps.

iii. Treated Powdered Gluten When the test was applied to this material, the bulk of it initially floated upon the surface and only slowly sank below. The dispersibility time was 3% hours. This could be shortened by vigorously agitating the material when it sank and disintegratedto form a relatively stable dispersion.

The contrast between the three sorts of gluten product (i to iii) in respect of wettability and dispersibility is illustrated in FIGS. 4 and 5. FIG. 4 shows the result, after a given time in seconds as indicated on the stopclock, of placing a spoonful of the powdered gluten and a spoonful of the agglomerated gluten on the surface of water in two beakers (A and B respectively) with gentle stirring of the contents at the same speed. Corresponding FIG. 5 shows the comparable result for treated powdered gluten and the agglomerated gluten (A and B respectively). As can be seen, in both instances, almost all the agglomerated gluten has sunk beneath the surface and, in moving toward the bottom of the beakers, has disintegrated and dispersed to form a relatively uniform slurry. In contrast thereto, the bulk of both the untreated and treated powdered gluten have remained floating on the surface of the water.

E. Dispersion Stability The stability, i.e. the resistance of individual particles in an aqueous dispersion of the agglomerated gluten to coalesce was determined by placing 5 gms. of the material in ml. distilled water at 20C., while stirring continuously with a mechanical stirrer operating at 350 rpm. For comparison, dispersions were formed in an identical manner with the same amount of untreated powdered gluten and treated powdered gluten (coated with 20% by weight monoglyceride). Following formation, the dispersions were allowed to stand for 24 hours prior to evaluating the stability of the dispersion as reflected in the extent to which individual particles stayed separated and distinct. Both the agglomerated gluten and the treated powdered gluten exhibited little coalescence between individual particles and remained in the form of a fairly uniformdispersion. This contrasted with the ordinary powdered gluten in which the particles had flocked together to give a more or less unified and intractable mass of hydrated gluten.

F. Porosity.

Reference has been made herein to the porous nature of the individual dluten agglomerates. A bulk mass of the agglomerates is likewise porous on account both of the porous nature of the agglomerates themselves, and bridging between the agglomerates which prevents a closely packed relationship and, gives rise to many interstitial spaces. The superior porosity of the agglomerated gluten compared to ordinary powdered gluten is demonstrated in the following test:

A glass tube mm. long and 16 mm. internal diameter was packed with gluten to a depth of 100 mm.; the

.gluten was tapped down firmly. With the tube in the verticalposition, 1 ml. of water was pipetted into the tube. The depth of penetration of the water, in mm.. into the sample after 30 seconds was noted. With a typ' ical sample of agglomerated gluten. the water penetrated 25 mm. in contrast to the 1 mm. penetration achieved in ordinary powdered gluten. This comparative test clearly demonstrates the superior porosity ol the agglomerated gluten.

H. Moisture Content The residual moisture content in the agglomerated gluten product is important in ensuring optimum dispersion of the agglomerated gluten in water; we have found that an agglomerated gluten with a moisture content in excess of 10% is less readily dispersed in water than agglomerated gluten with a lower moisture content. Preferably, the residual moisture content is between 6 and 8%, for then the agglomerated gluten often disperses spontaneously simply on addition to water and usually there is no need for even gentle stirring. Moisture levels of the agglomerated product also affect the wettability thereof. At levels below about to 6%, the agglomerated gluten does not wet, whereas at levels between about 6 and about 10%, wetting is very rapid with the product spontaneously sinking into the water as it disperses. Moisture levels beyond 10% are not desirable in view of the onset of rancidity upon storage. Ordinary powdered gluten typically has a residual moisture content of between 4 and 6%.

A still further characteristic of the agglomerated gluten is that its flavor and baking characteristics are not noticeably impaired by the agglomerating treatment, as will be demonstrated by the comparative tests in Examples hereinafter.

Summarising the characteristic and advantageous properties of the agglomerated gluten as compared with ordinary gluten powder, the functionality of the former is markedly superior because it is readily wetted and dispersed in water to form a relatively stable dispersion, i.e., reduced tendency to coalesce. For these reasons, it is ideally suited for use in the manufacture of yeastleavened bakery products, especially in continuous doughmaking break processes involving the initial formation of a liquid preferment or brew which includes essentially about one-half of the flour weight and a major proportion of the water of a dough formulation. The agglomerated gluten may be added directly to the brew without any difficulties associated with the wetting and dispersing thereof, or the formation of a foam, and maintained in a dispersed state simply with gentle agitation until final dough development takes place. The gluten is generally added in an effective amount up to 10% of the flour weight to achieve the desired dough supplementation.

The free-flowing character of the agglomerated gluten is reflected in the ease with which it can be removed from a package and poured without plugging or dusting.

The invention is further described in the following Examples, which, being illustrative are not intended to limit the scope of the invention, except as such limitations may appear in the appended claims.

EXAMPLE I Preparation of Agglomerated Gluten The method of our copending application Ser. No. 309,656 was used in a typical run to process a powdered gluten commercially available from Industrial Grain Products Limited, Thunder Bay, Ontario, Canada. The gluten was fed into the reactor at a rate of 600 lbs. per hour and formed into a fluidized bed by admitting heated air to the chamber through the diffuser plate at a constant rate of 40 f.p.m. Water in the form of droplets of a size 10 to 100 microns was sprayed into the fluidized bed through ten, two-fluid nozzles, each 12 delivering 1.5 i.g.p.h. water, utilizing air at a pressure of 35 p.s.i.g., as the atomizing agent. The temperature of the air entering the plenum chamber below the diffuser plate was about 1 15C. and the temperature of the gluten in the treatment chamber was about 46C.

The bulk of the gluten recovered from the above process was. in the form of dry, coarse, irregularly-shaped agglomerates at least of which were of a size greater than 149 microns.

That the agglomerated gluten so-obtained retains the original chemical properties of the original powdered gluten and differs therefrom only in certain advantageous physical properties is demonstrated by the results given in the following table which compares relevant properties of the agglomerated gluten with those of the initial powdered gluten.

Table 11 Comparisons of Properties 01' Agglomerated Gluten and Powdered Gluten Test! conducted mi described hcreinbefnre.

That the protein quality of the agglomerated gluten is unimpaired relative to the initial powdered gluten was shown by comparisons of Brabender farinographs of flour containing the same amount of agglomerated gluten of this Example, and the powdered gluten as well as, for illustrative purposes, a treated (20% by weight monoglyceride) powdered gluten of the prior art.

In each instance, 8% by weight of the given gluten was admixed with 92% by weight of untreated soft wheat flour. For control purposes, a farinograph was run on the soft wheat flour alone.

The farinograph curves are reproduced as FIGS. 6 to 9 of the accompanying drawings and the results are summarised in the Table below:

Table 111 Water Ab- A B C D E Product sorptlon (91) Soft wheat flour 52.5 1 1.5 3 4 35 Agglomerated 57.1 1 3 2.5 15.2 17 25 fluten ntreated powder gluten 56.8 1.5 3.5 16 17.5 5 Treated gluten 55.1 1.1 1.5 17.4 18 3O Absorption The absorption of water-holding capacity of the flour-gluten mixture is expressed as a perwhich any part of the curve is at or above the 500 BU consistency level.

D Departure Time Indicates the time in minutes from the start of mixing until top of farinograph band recrosses the 500 BU line.

doughs were derived from the following compositions:

Table IV Dough Composition Gluten Wheat Starch Water (gms) (gms) (cc) A 42.9 232.5 2l0.6 B 43.8 232.8 209.4 C 52.4 221.8 2ll.8

The wheat starch used was Supcrgell, commercially available from Industrial Grain Products Limited, Thunder Bay. Ontario, Canada.

A Agglomerated Gluten B Untreated Powdered Gluten is E gggi lgz f sfi i i i i f C Treated Powdered Gluten mm 8 P63 y o a The results of the extensograph analyses are summapomt 5 minutes after the peak. I used in the Table below.

t will be apparent upon comparison of the farinograph curves that the protein quality of the agglomer- Table v ated gluten is in no way inferior to that of the powdered Dough Resistance to Extensibility gluten, treated or untreated. Moreover, it will be noted Exmlsim that the agglomerated gluten has the highest water abhour BU hours g iz sorption capacity, which IS an important factor, espe- 5 cially in the baking industry, for such an increase per- 3 223 113% 3:35 mits the baker to increase his yield from a given weight C 526 307 4.58 4.20 of flour.

Further evidence as to the unimpaired protein quality of the agglomerated gluten is provided by Brabender It will be apparent upon comparison of the foregoing extensographs of compositions containing a given results thatthe quality of the agglomerated gluten has amount of the agglomerated gluten of this Example, ornot been deleteriously affected in the process of makdinary powdered gluten and powdered gluten treated ing it from the gluten powder starting material. with 20% by weight of a monoglyceride. These tests EXAMPLE 2 were conducted under standard conditions on a Brabencler extensograph which is a well-known device for Four samples of agglomerated gluten were prepared measuring and recording the extensibility and resisfollowing the basic procedure of Example 1 but emtance to extension of flour doughs. In this instance, the p y g, in the four runs. different Operating Conditions as summarised in the Table below:

Table VI Condition Run No. l Run No. 2 Run No. 3 Run No. 4

Airflow rate s.c.f.m./l'i.* 60 60 40 40 Temperature of inlet air (C) I37 I37 I37 ll5 Temperature of gluten (Ci (fluidized bed) SI 57 60 4s Gluten feed rate (lb. per hour) I00 I350 I300 Gluten particle size -18 l8 +80 l6 +i00 l6 +l00 Water feed rate (gal. per hour) 4 4 I] 20 Atomizing pressure (p.s.i.g.) 50 50 35 35 Various properties of the four samples of agglomerated gluten are summarised in the Table below:

Table VII Property Run No. l Run No. 2 run. No. 3 Run No. 4

Moisture 4.5 5.0 5.0 8.0 Protein (9%) (dry basis) 80.5 80.7 30.7 80 Ash (3%) (dry basis) 0.8 0.8 0.8 0.8 Colour Cream Cream Cream Cream Bulk Density [gm/cc.) .40 .40 .40 .36 Flowability (seconds) I3 I4 l3 l5 Dispersibility Good Good Good: Excellent needs needs needs spontangcntle gentle gentle eous Dispersion Stability g g stirring Can be resuspended with slight stirring after settling for 24 hours Table VII-continued Property Run No. l Run No. 2 run. No. 3 Run No. 4

Vitality Good Fair Good Good Sieve Analyses on 25 Not tested 2.2 on 40 5.9 30.2 on 60 32.0 37.4 on 80 42.2 t9.2 on I00 6.2 3.2 on 120 4.5 2.8 on I40 3.2 2.2 on I70 |.8 1.0 on 200 4.2 1.8 thru' 200 EXAMPLE 3 Table lX-continued The importance Of parttcle SIIZ and moisture content p a Size Moiswl-e w u of agglomerated gluten tn relation to wettability perfor- +80 h 4 I d mes 085 not WEI mance is shown with reference to the following exammesh 32 does Wm ple. For compartson, data IS also presented for un- +40 mcsh 7.0 sinks8twets treated ow rapidly p dered fluten and treated powdered gluten. +60 mesh 72 sinks & was The data presented tn Table Vlll below was obtained rapidly at using the following test method. A small funnel with an +80 h 6 8 '?Ri mes wets ra I exit orifice diameter of 140 mm. was p|aced 7.5 cm. 50mg sifiksyslowly above the surface of water l00gm) contained tn a beamesh more Sinks filqwly ker. A 10 gm. sample of gluten material was dropped zflm fig f into the funnel and onto the water surface. The time floats was measured for the wetting of the whole sample. +40 mesh i li tmme 18 C y Table VI 30 +60 mesh 8.0 sinks, wets immediately Sample Particle Size Moisture Wetting Time +80 mesh ks' vets rapt y Agglomerated +40 mesh 4.9 8 sec. m sh sin wcts gluten slowly +60 mesh 4.9 8 sec. +80 mesh 4.9 20 sec. 80 mesh 4.) 30 min. Agglomerated gluten mesh 8.6 4 sec. EXAMPLE 4 +60 mesh 8.6 3 sec. +80 mesh as 4 sec. The superior functionality of the agglomerated glu- A lomemed mesh B15 40 ten product of this invention in its application to the +40 mesh 127 2 5 baking industry in comparison with untreated powig mes: 2 ecdered gluten and treated powdered gluten was demon- 22 strated in a sponge dough bread-making process. The Untreated agglomerated gluten used was that described tn Exampimz 50 min ple 1. One of the treated powdered glutens comprised Lipid-treated powdered gluten coated with 20% monoglyceryl stea- POWdered gluten milk rate. For control purposes, the process was repeated Note: Thc+sign in" we ofthe m' particle size I upon the particwlth no added gluten ular sieve.

Table IX Particle Size Moisture Wettability +40 mesh 0 does not wet +60 mesh 0 does not wet +80 mesh 0 does not wet 80 mesh 0 does not wet +40 mesh 3.5 does not wot +60 mesh 3.9 does not wet Formulation content (gms.] Ingredients Sponge Dough Flour 240 [60 Sugar l2 Salt 8 Water 144 98 Yeast B Milk Powder l2 Shortening l2 Gluten" (4% of flour) 4 or B The flour was a 50-50 blend of hard and soft wheat flours (moisture content of H.591. 46% nsh. 10.2; protein) "The yeast food was til the Arkady Douhlc Strength type.

*"The agglomerated gluten product. the untreated and treated powdered glutens were added to the sponge at levels of 4% by weight in each case. based on the weight of the flour.

Formulation The sponge was made by mixing the sponge ingredients in the McDuffy bowl of a Hobart mixer for 5 minutes at low speed. This sponge wasset to ferment for 4 hours at 27C. The dough was then made by adding the dough ingredients to the spongepmixing 12 minutes at high speed. This dough was then rested for 15 minutes and scaled at 162g. for pup, loaf baking at 218C. for 25 minutes. It was noted that the agglomerated gluten was the most easily dispersed in the water RESULTS One hour after baking, the volume of each loaf was measured by rapeseeddisplacerne'nt. The loaves were judged the following day. Both external and internal characteristics were observed andrated'according to the standard scoring procedure of the American Institute of Baking. The total score (maximum of 100 for a perfect loaf) is the sum of the scores of the internal and external characteristics. Specific volume was calculated by dividing bread volume in cubic centimeters by dough weight in grams. The results are reported in the table below.

Table X Level Specific Total by flour Volume Bread Gluten Type weight) (cc/gm.) Score Agglomerated gluten 4 6.4 91 Untreated powdered gluten 4 6.4 90 Treated powdered gluten 4 6.2 89 Control No gluten 5.6 83

CONCLUSIONS It is apparent from the results quoted that the agglomerated gluten gave the best baking result, and that, in comparison with powdered gluten and the treated gluten, the agglomerated gluten had not lost any vitality in the process for preparing it.

EXAMPLE 5 Table XI Continuous Dough Formulation Content (lb) Ingredient Brew Dough Flour Water Yeast Ammonium sulfate Sugar Salt Gluten Milk Calcium Acid Phosphate Calcium Propionate Atmul Shortening Potassium Bromate Potassium lodate Similar to the flour used in Example 3.

18 PROCEDURE The brew which contained 40% of the total flour was made by mixing the various brew ingredients and then setting the mixture at 80F. The incorporation of the untreated powdered gluten was achieved by preblending with the flour. The brew was allowed to ferment at this temperature for 2% hours without agitation. During this period, hydration and relaxation (necessary for developing gluten functionality) occurred. The remainder of the flour, water, yeast, ammonium sulfate, sugar, salt and gluten and the other ingredients were combined in the usual manner at the incorporator. Processing conditions were identical to those usually employed. The developed doughs were extruded directly from the high-speed developer into tared pans, proofed for minutes and baked for 18 minutes at 218C.

RESULTS a. It was noted that the agglomerated gluten was more readily wetted and became more fully hydrated and relaxed than the monoglyceride coated gluten. The gluten was easily dispersed without the formation of lumps.

b. It was noted that the dry gluten added to the brew had an effect on the behaviour of this brew. Both the powdered vital wheat gluten and the agglomerated vital wheat gluten lowered the foaming properties of the fermenting brew. This was a distinct advantage since the generation of excessive foam leads to overflow of the brew from the preparation and storage tanks, a recognised problem in continuous bakery operations. The control brew which did not contain added gluten had a marked tendency to foam. And, not surprisingly, this tendency to foam was even more marked with the brew which contained the monoglyceride coated gluten. The amount of foaming was measured by determining the volume increase of the brew. With no gluten, the brew volume increased 70% and the brew collapsed and started to foam again. With gluten present (both the powdered and agglomerated), brew volume increased only 30%; with the monoglyceride coated gluten, the brew volume increased l00%.

c. All the bread obtained was of good quality, but that obtained using the agglomerated gluten was noticeably the best having the highest volume, strongest side-walls, a fine, uniform grain and a soft, velvety texture.

As examples 4 and 5 show, the agglomerated gluten product of this invention is well suited for application in the baking industry offering distinct and significant advantages over the ordinary powdered gluten and coated gluten products presently used.

It is of especial value for use in continuous doughmaking processes for it can be readily and conveniently incorporated in the liquid fermentation brew so tha1 the gluten has time to hydrate and relax which is needed for the development of its functionality in the dough system. Although in the foregoing descriptior reference has been made to the use of the agglomer ated gluten in the manufacture of bread, it will be un derstood that the product may be used in the manufac ture of other products, such, for example, as pasta ma terials.

Since it is not feasible to exemplify all possible variz tions of this invention, it will be understood that the invention is not limited to the specific embodiments illustrated herein.

What is claimed is:

l. A dry vital wheat gluten product in the form of coarse, porous, irregularly-shaped agglomerates having a moisture content of between about 6 and 10 percent and composed of a multiplicity of individual gluten particles adhered together in a random form and array, the major proportion of the agglomerates having a particle size exceeding 149 microns and up to a maximum of 500 microns, and said agglomerated gluten product being further characterised by the ease with which it can be dispersed in neutral aqueous dispersion having a pH between about 4 and about 8 by simply stirring to form a relatively stable dispersion in such a medium.

2. A gluten product as claimed in claim I, wherein at least percent of said agglomerates have a particle size in excess of M9 microns.

3. A gluten product as claimed in claim 2, wherein the gluten has a bulk density of less than 0.40 gms./cc, and a moisture content of between 6 and 8 percent.

4. The gluten product as claimed in claim I wherein the major proportion of said agglomerates have a particle size between about I60 and about 250 microns.

II! t t I 

1. A DRY VITAL WHEAT GLUTEN PRODUCT IN THE FORM OF COARSE, POROUS IRREGULARLY-SHAPED AGGLOMERATES HAVING A MOSITURE CONTENT OF BETWEEN ABOUT 6 AND 10 PERCENT AND COMPOSED OF A MULTIPLICITY OF INDIVIDUAL GLUTEN PARTICLES ADHERED TOGETHER IN A RANDOM FROM AND ARRAY, THE MAJOR PROPORTION OF THE AGGLOMERATES HAVING A PARTICLE SIZE EXCEEDING 149 MICRONS AND UP TO A MAXIMUM OF 500 MICRONS, AND SAID AGGLOMERATED GLUTEN PRODUCT BEING FURTHER CHARACTERISED BY THE CASE WITH WHICH IT CAN BE DISPERSED IN NEUTRAL AQUEOUS DISPERSION HAING A PH BETWEEN ABOUT 4 AND ABOUT 8 BY SIMPLY STIRRING TO FORM A RELATIVELY STABLE DISPERSION IN SUCH A MEDIUM.
 2. A gluten product as claimed in claim 1, wherein at least 90 percent of said agglomerates have a particle size in excess of 149 microns.
 3. A gluten product as claimed in claim 2, wherein the gluten has a bulk density of less than 0.40 gms./cc, and a moisture content of between 6 and 8 percent.
 4. The gluten product as claimed in claim 1 wherein the major proportion of said agglomerates have a particle size between about 160 and about 250 microns. 